Detail investigation of thermoelectric performance and magnetic properties of Cs-doped Bi 2 Sr 2 Co 2 O y ceramic materials

Bi2Sr2−xCsxCo2Oy materials with 0 ≤ x ≤ 0.15, have been fabricated via the classical ceramic technique. XRD results have indicated that undoped and Cs-substituted samples are composed of Bi2Sr2Co2Oy phase as the major one. Microstructural studies have demonstrated the formation of a liquid phase, which allows a drastic grain growth. This factor is responsible for a drastic improvement of relative density, reaching about 95% of the theoretical one for 0.125 Cs content. On the other hand, electrical resistivity has been reduced up to 14 mΩ cm at 650 °C for 0.125 Cs content, around 40% lower than the obtained in undoped samples. As a consequence, Seebeck coefficient has been decreased due to the raise in charge carrier concentration. The highest power factor at 650 °C (0.21 mW/K2 m) has been found for 0.125 Cs substituted sample, about 40% larger than the obtained in undoped samples, and very similar to the notified in single crystals (0.26 mW/K2 m). Magnetisation with respect to temperature results have demonstrated that measured samples have a paramagnetic property above 50 K, except 0.10 Cs. Magnetic hysteresis curves have shown that the slopes and the magnitudes have increased with decreasing temperature.