Strong Composition Effects in All-Polymer Phototransistors with Bulk Heterojunction Layers of p-type and n-type Conjugated Polymers

We report the composition effect of polymeric sensing channel layers on the performance of all-polymer phototransistors featuring bulk heterojunction (BHJ) structure of electron-donating (p-type) and electron-accepting (n-type) polymers. As an n-type component, poly(3-hexylthiopehe-co-benzothiadiazole) end-capped with 4-hexylthiophene (THBT-4ht) was synthesized via two-step reactions. A well-studied conjugated polymer, poly(3-hexylthiophene) (P3HT), was employed as a p-type polymer. The composition of BHJ (P3HT:THBT-4ht) films was studied in detail by varying the THBT-4ht contents (0, 1, 3, 5, 10, 20, 30, 40, and 100 wt %). The best charge separation in the P3HT:THBT-4ht films was measured at 30 wt % by the photoluminescence (PL) study, while the charge transport characteristics of devices were improved at the low THBT-4ht contents (<10 wt %). The photosensing experiments revealed that the photosensivity of all-polymer phototransistors was higher than that of the phototransistors with the pristine P3HT la...