Surface characteristics and electrochemical behaviour of sputter-deposited NiTi thin film
2015
Thin nanocrystalline amorphous NiTi film was deposited on Si substrate using DC magnetron sputtering. The as-deposited NiTi thin film was crystallized by heat treatment at 500 °C for 1 h. The crystal structure, surface morphology, microstructure and surface chemistry of the deposited films were studied using X-ray diffraction, atomic force microscopy, scanning electron microscopy and X-ray photoelectron spectroscopy (XPS), respectively. Corrosion behaviour was assessed in Ringer’s solution at 37 °C by open circuit potential (OCP), potentiodynamic polarization and electrochemical impedance spectroscopy as a function of exposure time. OCP values indicate that the tendency for the formation of a spontaneous oxide film is greater for the NiTi thin films than the bulk NiTi. Long time exposure to Ringer’s solution was found to have a great effect on the corrosion behaviour of the samples. Significantly low corrosion current density was obtained for the annealed NiTi film from the potentiodynamic polarization cu...
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
58
References
7
Citations
NaN
KQI