Study of paramagnetic defect centers in as-grown and annealed TiO2 anatase and rutile nanoparticles by a variable-temperature X-band and high-frequency (236 GHz) EPR

Abstract Detailed EPR investigations on as-grown and annealed TiO 2 nanoparticles in the anatase and rutile phases were carried out at X-band (9.6 GHz) at 77, 120–300 K and at 236 GHz at 292 K. The analysis of EPR data for as-grown and annealed anatase and rutile samples revealed the presence of several paramagnetic centers: Ti 3+ , O − , adsorbed oxygen (O 2 − ) and oxygen vacancies. On the other hand, in as-grown rutile samples, there were observed EPR lines due to adsorbed oxygen (O 2 − ) and the Fe 3+ ions in both Ti 4+ substitutional positions, with and without coupling to an oxygen vacancy in the near neighborhood. Anatase nanoparticles were completely converted to rutile phase when annealed at 1000° C, exhibiting EPR spectra similar to those exhibited by the as-grown rutile nanoparticles. The high-frequency (236 GHz) EPR data on anatase and rutile samples, recorded in the region about g =2.0 exhibit resolved EPR lines, due to O − and O 2 − ions enabling determination of their g -values with higher precision, as well as observation of hyperfine sextets due to Mn 2+ and Mn 4+ ions in anatase.