Temperature dependence of coercivity of cellular Sm2Co17−SmCo5 permanent magnets

The spontaneous magnetization and the coercive field of sintered Sm(Co, Fe, Cu, Zr)7.6 alloys of cellular microstructure which were annealed at 775°C (sample A1) and also at 400°C (sample A2), were measured in the temperature range between 4.2and 1200 K. Materials A1 show an intrinsic type magnetic hardness with exponential type temperature dependence at cryogenic temperatures. Samples given subsequent heat treatments at lower temperatures (A2) show a more or less linear temperature dependence of the coercive field resulting in μ0HC = 7.6 T at 4.2 K. Implications of these findings for an understanding of the magnetic hardening process in cellular magnets are discussed. Die spontane Magnetisierung und die Koerzitivfeldstarke von gesinterten Sm(Co, Fe, Cu, Zr)7.6−Legierungen mit zellularer Mikrostruktur wurden, nach einer Warmebehandlung bei 775°C (Probe A1) und bei 400°C (Probe A2), im Temperaturbereich zwischen 4,2 und 1200 K unter-sucht. Die Probe A1 zeigtbei tiefen Temperaturen einen intrinsischen magnetischen Hartungs-mechanismus mit einer exponentiellen Temperaturabhangigkeit. Bei tieferen Temperaturen zeigen warmebehandelte Proben (A2) naherungsweise eine lineare Temperaturabhangigkeit der Koerzitivfeldstarke mit μ0Hc = 7,6 T bei 4,2K. Die Bedeutung dieser Ergebnisse fur das Verstandnis der magnetischen Hartungsprozesse in Zellularmagneten werden diskutiert.