Fabrication and characterization of Au/SBT/LZO/Si MFIS structure

Ferroelectric SrBi2Ta2O9 (SBT) films on a p-type Si (100) wafer with a LaZrOx (LZO) buffer layer have been fabricated to form a metal-ferroelectric-insulator–semiconductor (MFIS) structure. The LZO thin film and SBT films were deposited by using a sol–gel method. The equivalent oxide thickness (EOT) value of the LZO thin film was about 8.83 nm. Also, the leakage current density of the LZO thin film is about 3.3 × 10−5 A/cm2 at bias sweeping voltage of ±5 V. SBT films were crystallized in polycrystalline phase with highly preferred (115) orientation. Also, the intensity of each pick slightly increased as thickness of SBT films increased. The C–V characteristics of Au/SBT/LZO/Si structure showed clockwise hysteresis loop. The memory window width increased as the thickness of SBT films increased. The leakage current density of Au/SBT/LZO/Si structure decreased as thickness of SBT films increased.