Nickel assisted sintering of Ti3SiC2 powder under pressureless conditions
2010
Abstract This investigation was aimed to study the effect of nickel addition on the sintering behaviour of Ti 3 SiC 2 powder under pressureless conditions. Nearly pure bulk Ti 3 SiC 2 ceramic with relative density of ∼98.5% was produced at 1500 °C by sintering of Ti 3 SiC 2 powder while using 1 wt.% nickel as a sintering aid. The activation energy of sintering of Ti 3 SiC 2 powder was determined to be 351 ± 5 kJ/mol, which was decreased slightly to 305 ± 10 kJ/mol when nickel (1 wt.%) was added. Sintering of Ti 3 SiC 2 powder was found to be controlled by mixed mode of mechanisms, i.e., the interface reactions and diffusion of Si atoms. The mechanism was changed to liquid phase sintering due to melting of Ni-based compounds in the sample sintered with Ni. The reaction of Ni with Ti 3 SiC 2 helped to decrease the grain growth rate. The hardness (Vickers), flexural strength and fracture toughness of the sintered Ti 3 SiC 2 –1Ni sample were found to be 3.4 GPa, 311 ± 22 MPa and 2.8–6.4 MPa m 1/2 , respectively.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
43
References
10
Citations
NaN
KQI