Size-controlled InGaN/GaN nanorod array fabrication and optical characterization

We demonstrate a cost-effective top-down approach for fabricating InGaN/GaN nanorod arrays using a wet treatment process in a KOH solution. The average diameter of the as-etched nanorods was effectively reduced from 420 nm to 180 nm. The spatial strain distribution was then investigated by measuring the high-resolution cathodoluminescence directly on top of the nanorods. The smaller nanorods showed a higher internal quantum efficiency and lower potential fluctuation, which can subsequently be exploited for high-efficiency photonic devices.