Domain structures associated with the twinned phases V8N and V4N

The system V–N is investigated by X-rays, electron diffraction, and electron microscopy in the composition range 0 up to 25 at% N. The solid solubility of nitrogen is determined in the temperature range 500 up to 1200 °C. Two phases are formed upon quenching. The first is the V8N tetragonal phase. A supercell of the vanadium cell is proposed (a = b = 2ao √2, c = co). The transformation b.c.c. b.c.t. gives rise to a particular twinned configuration. The domains are related by a reflection twin (101)t, taking into account a supplementary rotation due to the tetragonal deformation. A new pseudo-orthorhombic phase V4N is analysed. This phase is isomorphous to Ta4N. The domain structure is described using a reflection twin (110)o and a rotation twin (130)o. Le systeme vanadium-azote a ete etudie dans le domaine de composition 0 a 25% atomique d'azote par rayons X, microscopie et diffraction electronique. La limite de solubilite a ete determinee pour les temperatures comprises entre 500 et 1200 °C. Deux phases se forment par trempe. L'une d'entre elles, V8N, est quadratique et une maille multiple de celle du vanadium est proposee (a = b = 2ao √2, c = co). La transformation cubique centre quadratique centre s'accompagne d'une configuration de macle particuliere. Les domaines sont relies par une operation de macle (101)t et une rotation supplementaire consecutive a la deformation quadratique. Une nouvelle phase pseudo-orthorhombique, V4N, a ete obseree et analysee. Cette phase est isomorphe de la phase Ta4N. La structure en domaines est expliquee au moyen de deux operations de macle: une macle de reflexion (110)o et une macle de rotation (130)o.