Exploring the influence of Al content on the hot deformation behavior of Fe-Mn-Al-C steels through 3D processing map

Abstract The effect of Al content on the hot deformation behavior of high-Mn low density Fe Mn Al C steels was investigated by the 3D processing map at the temperatures of 850–1050 °C and the strain rates of 0.001–10s −1 . The high-Al steel showed a higher flow stress and a greater activation energy (443 kJ/mol) in contrast to the low-Al steel (394 kJ/mol). The microstructures of 8Al steel and 10Al steel depends on the deformation parameters. The initial hot rolling microstructure has been displaced by the recrystallized structure and substructures for both steels, while the unstable zone has deformation bands and flow localization. As the Z content increases with increasing Al content, this leads to a significant inhibition of the DRX process, resulting in an unstable domain with deformation zones and flow localization. For high-Al steel, the morphology and distribution of ferrite transform from the continuous band ferrite to discontinuous granular ferrite, moreover, the flow localization features cannot be observed with the decrease of strain rate to 0.001s −1 . Furthermore, the proportion of instability region for each of the strains increases with the increasing of the Al content, the high Al content weakens the workability of the Fe Mn Al C steels.