Multi-Stage Cold Deep Drawing of Pure Titanium Square Cup

This paper deals with the formability of pure titanium sheet in square cup deep drawing. Pure titanium has very excellent corrosion resistance. In the metal forming process, pure titanium has very good ductility in cold forming. The normal anisotropy of pure titanium is very high. Therefore, the property is suitable to the sheet metal forming, such as deep drawing process. However, the most important problem is that the occurrence of seizure becomes remarkable in severe forming operations. Many investigations on the effect of processing conditions on the seizure of titanium were carried out. In the present study, the formability of pure titanium sheet in square cup deep drawing was investigated. For the prevention, pure titanium sheets were treated by heat oxide coating. The fresh and clean titanium is not in direct contact with the die during the forming due to the existence of the oxide layer. The material was pure titanium sheets of the JIS grade 2. The initial thickness of the blank was 0.5 mm in thickness. In the deep drawing process, the sheets were employed and a flat sheet blank is formed into a square by a punch. Forming of sheet by multi-stage deep drawing was tried. Various cups were drawn by exchanging the punch and die. The die was taper without a blankholder in the subsequent stages. The effects of the intermediate annealing and tool shape on the occurrence of seizure in square cup deep drawing were also examined. The square cups were successfully drawn by heat oxide coating. The coating of titanium sheet has sufficient ability in preventing the seizure in multi-stage deep drawing operation. The results of the present study revealed that the pure titanium square cups were successfully formed by using heat oxide coating treatment.