Temperature-Dependence of Corrosion of Ni-Based Superalloys in Hot CO 2 -Rich Gases Containing SO 2 Impurities

Future power plants will require Ni-based superalloys resistant to high-temperature corrosion in CO2-rich environments containing impurities. In this work, several commercially available Ni-based alloys (617, 230, 625, 263, 740H) were exposed at 600°C, 650°C, 750°C and 1 atm to 95% CO2, 4% H2O, 1% O2 without/with 0.1% SO2 to simulate compositions expected in a direct-fired supercritical CO2 power cycle. The results indicate no effect of SO2 at 750°C, a small negative effect at 650°C, and a large negative effect at 600°C. Alloys exposed at the higher temperatures (650–750°C) formed thin Cr-rich oxide scales, whereas the lowest temperature (600°C) resulted in thicker scales consisting of non-protective oxides and sulfates. Thermodynamic analysis indicates this increased corrosion is associated with a transition in the stable compounds in contact with the gas. Understanding the factors that affect this transition will aid in the selection or design of alloys for future CO2-based power systems.