Gamma radiation curing of nitrile rubber/high density polyethylene blends

Nitrile butadiene rubber (NBR) was mixed with high density polyethylene (HDPE) thermoplastics with different ratio namely (100/20), (100/40), (100/60) and (100/80). The obtained blends were subjected to gamma irradiation with varying dose from 50 to 250 kGy. The induced crosslinking and hence the improvement in the different properties were followed up as a function of irradiation dose. Mechanical properties as tensile strength, tensile modulus at 50 % elongation, elongation at break percent, permanent set and hardness were carried out as a function of irradiation dose and blend ratio. Moreover, physical properties namely, gel fraction % and swelling number were found to improve with the increase of irradiation dose up to 250 kGy and with the increase of the content of HDPE in blend. Moreover, presence of NBR enhances the shrinking properties of the obtained blend which can be used as a good heat shrinkable material.