Interlayer strain effects on the structural behavior of BiFeO3/LaFeO3 superlattices

Artificial (BiFeO3)0.5Λ/(LaFeO3)0.5Λ superlattices have been grown by pulsed laser deposition. The periodicity Λ was varied from 150 A to 25 A and the relative ratio between BiFeO3 (BFO) and LaFeO3 (LFO) is kept constant in each period. X-ray diffraction, transmission electron microscopy, and Raman spectroscopy investigations indicate antiferroelectric-like structures for large periodicity (Λ ≥ 76 A), while Pnma LaFeO3-like structures are observed for small periodicity Λ ≤ 50 A. Room temperature magnetic measurements were obtained by vibrating sample magnetometry and suggest antiferromagnetic ordering with weak ferromagnetism. Temperature dependent x-ray diffraction studies show an important shift of paraelectric-antiferroelectric phase transition scaling with BFO thickness. Strain and size effects explain this behavior and discussion is also made on the possible role of the oxygen octahedral rotation/tilt degree of freedom.