In-situ kinetics study on the growth of expanded austenite in AISI 316L stainless steels by XRD

The formation of expanded austenite in Cr-Ni austenitic stainless steels like AISI 316L is not completely understood despite its technological relevance. In this work, we present an in-situ X-ray diffraction study on the growth kinetics of the expanded austenite. We applied a low-temperature nitrocarburizing treatment using a mixture of NH3, N2, H2, and C2H4 gases at atmospheric pressures in a novel and custom built chamber attached to a Bruker D8 Advance diffractometer. The nitrocarburizing temperature was varied between 340 and 440 °C, and the possible effects of the gas amount were also tested. The thickness of the growing layer was determined from the shrinkage of the unmodified austenite peak. The growth rate coefficient was calculated using the linear-parabolic equation. The resulting coefficients follow the Arrhenius law with the activation energy of 165 ± 12 kJ/mol. This value is in good agreement with the diffusion activation energy for heavy interstitials like carbon and nitrogen. The expanded a...