Tribo-investigation on PTFE lubricated PEEK in harsh operating conditions

A series of blends with Polytetrafluroethylene (PTFE) powder and Polyetheretherketone (PEEK) was developed by varying the PTFE contents in steps of 5 wt.% from 0 to 20 wt.%. The composites were evaluated for their friction and wear properties at room temperature as well as high temperature in low amplitude oscillating wear (LAOW) mode against steel (100 Cr 6) ball against polymer plate. The same blends were also evaluated in abrasive wear mode to study the influence of harsh operating conditions on wear and friction performance. Incorporation of PTFE benefited PEEK in various ways such as it increased the tribo-utility of the latter by increasing its limiting load value, removing its stick-slip tendency, lowering coefficient of friction and specific wear rate significantly. With increase in PTFE content, benefits to the wear performance increased regularly. This was not the case for friction coefficient. Lowest μ was recorded for 15% PTFE contents. The enhancement in wear and friction performance, however, was at the cost of strength properties which decreased substantially with increase in PTFE content. At 100 °C, friction coefficient and wear rates of all blends increased marginally. In abrasive wear mode, on the other hand, PTFE filled PEEK showed poorer wear resistance than neat PEEK. This was correlated with strength properties and it was observed that these blends closely followed the predictions of Ratner–Lancaster plot. SEM was used to examine the micro-structural features of worn surfaces.