Influence of TiO2 on Viscosity, Phase composition and Structure of Chromium-containing high-titanium Blast Furnace Slag

Abstract The viscous flow of CaO–SiO2–Al2O3–MgO–TiO2–Cr2O3 slag (CaO/SiO2=1.1, Cr2O3=0.5 mass%) were investigated to promote understanding of the effect of TiO2 addition on the viscous behavior of chromium-containing vanadium-titanium blast furnace slag. The viscosity of the slag was measured using a rotating crucible viscometer. Raman spectroscopy analysis was performed to correlate the viscosity to slag structure. The viscosity of slag was found to significantly decrease with increasing TiO2 content at a fixed basicity. It is because the Ti4+ continuously detached from the network structure, the content of [Ti2O6]4- decreased, and the content of [TiO4]4- tetrahedral monomer increased, which made the slag structure simplified. Consequently, the polymerization degree of the slag decreases with increasing TiO2 content. The variation in slag structure is consistent with the change in measured viscosity.