The Generation Ability of Liquid Phase for Mixture of Iron Ore Powders and Lime: Prediction, Characterization and Influencing Factors
2015
The fraction of liquid phase in sintered ore can be the most important factor to determine the sinter quality and yield in sintering process. The generation ability of liquid phase for mixture of iron ore powders is determined by basicity, roasting time, roasting temperature and chemical composition of iron ores. Five different iron ores were selected in this study and the dried powders of iron ore and CaO reagent (<200 mesh) were homogeneously mixed together at their required proportions, then 15g of the mixture was pressed under a pressure of 20MPa to make a cylindrical sample with a diameter of 20mm. The sintering temperature in this study was kept at 1280°C, the gas phase is air, the holding time was varied with its three levels of 5min, 10min and 15min. After that, the sample was cooled under room temperature in the air, and the cooled sample was analyzed by using zeiss optical microscope. The mineral phase compositions were quantitatively determined with an open source image processing software, Image J whicn can calculate the fraction of liquid phase. Besides, the study on how to estimate the sintering behavior of the raw materials in different conditions by the theoretical calculation is of vital importance, and the development of this will greatly improve the sintering production. Factsage will be used to calculate the liquid phases formulation during the sintering. Comparing the experimental results and the theoretical calculation shows that the mass of liquid phase increases with increasing basicity during the sintering, besides, the mass of calcium ferrite increases with increasing basicity. The generation ability of liquid phase of iron ores can be predicted through the experiment verification.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
7
References
0
Citations
NaN
KQI