A Comparative study of the firing shrinkage properties of the process temperature control rings

A process temperature control ring was developed from talc, magnesium carbonate, barium carbonate, iron oxide, kaolin, and quartz.  The rings were formed by the dry pressing method into a diameter of 2.5 cm and with the density of 1.8 g/cm 3 .  The firing shrinkages of rings at 960°C, 1100°C, 1140°C, and 1200°C varied in the range of 2.21-9.98 % with the standard deviation varied in the range of 0.00-0.06. In this study, the properties of the rings were statistical analyzed. It was found that an increasing temperature resulted in an increasing firing shrinkage but  no effect on the standard deviation values.  The study also presented the comparative properties of the rings with the commercial ones in terms of the average firing shrinkage, the standard deviation and the change of the shrinkage with temperature. บทคดยอ อปกรณตรวจสอบอณหภมแบบวงกลมไดพฒนาจากสตรทประกอบดวย ทลคม แมกนเซยมคารบอเนต แบเรยมคารบอเนต เหลกออกไซด ดนขาว และควอตซ เปนองคประกอบ ขนรปอปกรณฯดวยวธอดแหงใหไดขนาดเสนผานศนยกลาง 2.5 ซม. ความหนาแนน 1.8 กรม/ลบ.ซม. ตวอยางมสมบตการหดตวเมอเผาทอณหภม 960 C, 1100 C,1140 C และ 1200 C อยในชวงรอยละ 2.21-9.98 และมคาสวนเบยงเบนมาตรฐาน 0.00-0.06 งานวจยนไดใชสถตในการประมวลผลสมบตของอปกรณฯทพฒนาเมอเผา พบวาการเพมอณหภมมผลใหการหดตวเมอเผาเพมขน แตไมมผลตอคาสวนเบยงเบนมาตรฐานของการหดตวเมอเผา งานวจยนยงไดแสดงขอมลเปรยบเทยบสมบตของอปกรณฯทพฒนากบอปกรณฯทจำหนายในทองตลาด ในคาเฉลยของการหดตวเมอเผา คาสวนเบยงเบนมาตรฐานของการหดตว เมอเผา และการเปลยนแปลงของคาการหดตวเมอเผากบระดบอณหภม