알루미나이드 확산코팅된 스테인레스 합금의 내산화 및 내삭마 특성

Stainless steel, a type of steel used for high-temperature parts, may cause damage when exposed to high temperatures, requiring additional coatings. In particular, the Cr2O3 product layer is unstable at 1000oC and higher temperatures; therefore, it is necessary to improve the oxidation resistance. In this study, an aluminide (Fe2Al5 and FeAl3) coating layer was formed on the surface of STS 630 specimens through Al diffusion coatings from 500oC to 700oC for up to 25 h. Because the coating layers of Fe2Al5 and FeAl3 could not withstand temperatures above 1200oC, an Al2O3 coating layer is deposited on the surface through static oxidation treatment at 500oC for 10 h. To confirm the ablation resistance of the resulting coating layer, dynamic flame exposure tests were conducted at 1350oC for 5–15 min. Excellent oxidation resistance is observed in the coated base material beneath the aluminide layer. The conditions of the flame tests and coating are discussed in terms of microstructural variations.