YbBa2-xSrxCu3O7-δ coated conductor development by sol-gel process
2005
YbBa 2-x Sr x Cu 3 O 7-δ coated conductors were grown on Gd 1.8 Ho 0.2 O 3 buffer layered biaxially textured-Ni (100) substrates by the reel-to-reel sol-gel dip coating system. Sample with different Sr substitution ratio (x = 0.0, 0.1, 0.2, 0.3, 0.4, and 0.6) were heat treated using varying heat treatment parameters. The surface morphologies and microstructure of all samples were investigated by ESEM, EDS and XRD. The critical current measurements were performed using four-wire method with the 1 μV/cm criterion. The critical current density, J c was measured to be 10 5 A/cm 2 at 4.2 K and 10 4 A/cm 2 at 75 K in-self field for YbB 1.9 Sr 0.1 Cu 3 O 7-δ sample.