Enhanced thermoelectric performance of Na-doped PbTe synthesized under high pressure

Despite an effective p-type dopant for PbTe, the low solubility of Na limits the fully optimization of thermoelectric properties of Na-doped PbTe. In this work, Na-doped PbTe was synthesized under high pressure. The formation of the desired rocksalt phase with substantially increased Na content leads to a high carrier concentration of 3.2×1020 cm−3 for Na0.03Pb0.97Te. Moreover, dense in-grain dislocations are identified from the microstructure analysis. Benefited from the improved power factor and greatly suppressed lattice thermal conductivity, the maximal ZT of 1.7 is achieved in the optimal Na0.03Pb0.97Te. Current work thus designates the advantage of high pressure in synthesizing PbTe-based thermoelectric materials.