The effects of annealing temperature and heating rate on Ta/TbFeCo bilayers

Among various perpendicularly anisotropic magnetic materials, amorphous rare earth-transition metal RE-TM alloys have attracted much interest due to the advantages of tunable magnetic properties and suitable perpendicular magnetic anisotropy (PMA) strength. In this study, the magnetic properties of the Ta/TbFeCo/MgO structure with various Tb-contents are investigated under different annealing conditions like heating rate and annealing temperature. The samples were annealed at heating rate from 10 °C/min to 50 °C/min and holding time was varied from 10 min to 30 min with annealing temperatures ranging from 100 to 150 °C. We found that fast heating rate and low holding temperature help to improve PMA and significantly increase the saturation magnetization and squareness of the TbFeCo films.Among various perpendicularly anisotropic magnetic materials, amorphous rare earth-transition metal RE-TM alloys have attracted much interest due to the advantages of tunable magnetic properties and suitable perpendicular magnetic anisotropy (PMA) strength. In this study, the magnetic properties of the Ta/TbFeCo/MgO structure with various Tb-contents are investigated under different annealing conditions like heating rate and annealing temperature. The samples were annealed at heating rate from 10 °C/min to 50 °C/min and holding time was varied from 10 min to 30 min with annealing temperatures ranging from 100 to 150 °C. We found that fast heating rate and low holding temperature help to improve PMA and significantly increase the saturation magnetization and squareness of the TbFeCo films.