Solvothermal synthesis of large surface area zirconia

The reaction of zirconium n-propoxide in glycol at 300°C yielded microcrystalline tetragonal zirconia (ZrO2). The crystallite size of the product depended on the carbon number of the glycol and increased in the following order (carbon number of glycol): 2<6<4, which suggested that the heterolytic cleavage of O-C bond of gylcoxide formed by transesterification is the prime factor for the formation of the product. In toluene, zirconium isopropoxide also gave tetragonal zirconia at 300°C, and zirconium tert-butoxide decomposed at 200°C yielding amorphous zirconia, while zirconium n-propoxide was stable at 300°C. These results suggest that the reaction in toluene depends on the structure of the alkyl group of the alkoxides. Thus-obtained tetragonal zirconias maintained large surface areas (90–160 m2/g) even after calcination at 500°C.