Stabilization of Nickel-Rich Layered Cathode Materials of High Energy Density by Ca Doping

Lithium-ion batteries have been considered the most important devices to power mobile or small-sized devices due to their high energy density. LixCoO2 has been studied as a cathode material for the Li-ion battery. However, the limitation of its capacity impedes the development of high capacity cathode materials with Ni, Mn, etc. in them. The substitution of Mn and Ni for Co leads to the formation of solid solution phase LiNixMnyCo1-x-yO2 (NMC, both x and y 0.8 in the metal site), poor cycle retention capability still remains to be overcome. In this study, aiming to improve the stability of the physical and chemical bonding, we investigate the stabilization effect of Ca in the Ni-rich layered compound Li(Ni0.83Co0.12Mn0.05)O2, and then Ca is added to the modified secondary particles to lower the degree of cationic mixing of the final particles. For the optimization of the final grains added with Ca, the Ca content (x = 0, 2.5, 5.0, 10.0 at.%) versus Li is analyzed.