Influence of annealing temperature on the microstructure and magnetic properties of Ni/NiO core-shell nanowires

Abstract Ni/NiO core-shell nanowires (NWs) were synthesized by thermal annealing of Ni NWs and variations in the microstructure, surface morphology, and magnetic properties of the NWs as a function of annealing temperature were investigated. The results showed that the grain size and crystal quality of NiO increased with an increasing annealing temperature. Specially, the effect of annealing temperature was much greater than annealing time for the formation of Ni/NiO NWs during the oxidization process. The total weight gain of the Ni/NiO NWs continuously increased when the annealing temperature was lower than 400 °C and the annealing time was more than 2 h; however, the weight gain of the Ni/NiO NWs was almost constant after annealing for 40 min when the annealing temperature was higher than 500 °C. The thorns on the surface of the Ni/NiO NWs gradually passivated and magnetic properties declined when the annealing temperature was increased from 300 °C to 400 °C. Smooth Ni/NiO NWs with no magnetic properties were prepared when the annealing temperature was over 500 °C. The detail study regarding the formation and evolution of Ni/NiO NWs is of considerable value and may provide useful information regarding the choice of post-treatment parameters for different applications of Ni/NiO NWs.