The Segregation of Poly(styrene-b-isoprene) Diblock Copolymers to the Surface of a Polystyrene Melt: the Effect of the Ratio of Block Lengths

The effect of the ratio of block lengths on the interfacial partitioning of poly(styrene-block-1,4 isoprene) diblock copolymers from their mixtures with polystyrene homopolymer melt is investigated utilizing a series of copolymers with almost constant molecular weight but different compositions. The concentration profile of the copolymer is measured directly using the \(\) nuclear reaction analysis technique; a segregation of the diblock is found at both the air/polymer surface, due to the lower surface energy of polyisoprene, and at the substrate/polymer interface. No significant effect of the block length ratio on the free-surface excess was observed. The block molecular weights have apparently led to dangling chain conformations in the non-overlapping mushroom and in the overlapping mushroom regimes whereas the brush regime was not accessible; no indications of a real border between the two former regimes was found.