Deuterium Retention Properties of Co-Deposited Carbon Films Produced at Wall Gaps ∗)

Deuterium retention properties in co-deposited carbon film produced in gap and the relationship between this retention behavior and the crystal structure of carbon film were investigated. In the case of a wide gap, the atomic ratio of deuterium to carbon (D/C) in the film was almost constant at any depth in the gap, while in the case of a narrow gap the D/C ratio decreased with increasing distance from the gap entrance. The micro structure of carbon film tended to be more amorphous for the film produced at locations deeper in the gap. Thermal desorption spectra of D2 in the film produced near the gap entrance showed one broad main peak at around 1100 K, while that in the film produced near the bottom showed very sharp peaks at around 950 K. This difference in desorption behavior was related with the differences of micro structure.