Enhanced As(III) sequestration using nanoscale zero-valent iron modified by combination of loading and sulfidation: characterizations, performance, kinetics and mechanism

Nanoscale zero-valent iron (nZVI) and sulfides have been confirmed to be effective in arsenic sequestration from aqueous solution. In this study, attapulgite supported and sulfide-modified nanoscale zero-valent iron (S-nZVI@ATP) are synthesized to realize the superposition effect of enhanced arsenic sequestration. The results indicated that nZVI clusters were well disaggregated and the BET specific surface area increased from 19.61 m2·g-1 to 46.04 m2·g-1 of S-nZVI@ATP, resulting in an enhanced removal efficiency of arsenic from 51.4% to 65.1% at 20 min. The sulfides in S-nZVI@ATP mainly exist as mackinawite (FeS) and this causes the spherical nanoparticles to exhibit a larger average particle size (94.6 nm) compared to bare nZVI (66.0 nm). In addition, S-nZVI@ATP exhibited a prominent ability for arsenic sequestration over a wide pH range of 3.0-6.0. The presence of anions SO42- and Cl- can enhance the arsenic removal whereas HCO3- inhibited it. The arsenic adsorption by S-nZVI@ATP could be explained by the pseudo-second-order kinetic model and the Langmuir model, with the maximum adsorption capacity of 193.8 mg·g-1. The mechanism of As(III) sequestration by S-nZVI@ATP involved multiple processes, mainly including precipitation conversion from FeS to As2S3, surface-complexation adsorption and co-precipitation.