Bond strength and durability of universal adhesive agents with lithium disilicate ceramics: A shear bond strength study

AbstractThe aim was to assess the shear bond strength (SBS) of lithium disilicate (LD) ceramic to resin composite with different universal adhesives, duration of ageing and silane. One hundred and twenty LD ceramic discs were processed, fired and etched (HF acid 5%) for 20 s (sec). All specimens were divided into 12 groups (n = 10), based on different combinations of, 3 different universal adhesives [Scotchbond (SB) Universal Adhesive, All-Bond (AB) Universal, and Futurabond U (FU)], silane and different duration of ageing [24 h and 3 months]. Composite resin cylinders (Tetric ceram) (3mm × 2 mm) were formed using bonding jig on ceramic and were light-cured. The specimens in groups 1–6 and 7–12 were stored in distilled water (37 °C) for 24 h and 3 months (thermocycling -5000 cycles 5–55 °C/30 s dwell time) before being subjected to bond strength testing respectively. Using universal testing machine shear bond test was performed at a crosshead speed of 1 mm/min. Failure modes and fracture patterns were ass...