Thermooxidative stabilization of a MDI

Samples of flexible PU foam were prepared from a polyol (Elastoflex W 5516/115) and an isocyanate prepolymer (Iso 145/8), both commercial Elastogram products. For the thermooxidative stabilization, two phenolic compounds were used, separately or in mixture. These compounds were: 2,6-di-t-butyl-4-methyl-phenol (non-reactive) (AO-1), 3,5-di-t-butyl-4-hydroxy-benzyl alcohol (reactive, AO-2), used in total mass% of 0.3/1.5. The TG/DTG/DTA curves were drawn up in dynamic air, with a heating rate of 10 °C min−1, until 500 °C. For the unstabilized sample a single thermodegradative TG step, with a maximum rate at 268–270 °C was observed, whereas for the stabilized samples, supplementary steps at higher temperature were observed. The changes in the TG/DTG/DTA parameters are not in a single relationship with the mass% of the stabilizator, due to the following: AO-1 is easily migrated out from PV, especially, at higher concentrations. AO-2 had positive effect at all studied concentrations. But the most remarkable effect is the synergetic effect of a 1:1 mixture of AO-1 and AO-2.