Sol—Gel Synthesis of Strontium‐Doped Lanthanum Manganite

This paper reports on strontium-doped lanthanum manganite powders that were prepared using a peroxide acetate salt based solution. The stable sol was peptized by reacting ammonium hydroxide with the precursor solution. The amorphous dried gel powders exhibit a high energy level, due to their high cations coordination and small particles, to develop the perovskite phase. This crystalline phase development from powders containing monocarboxylate ligands was characterized by thermal analysis (TG, DTG, DTA), X-ray diffraction, and IR spectroscopy. The transformation from amorphous powders into a crystallized homogeneous oxycarbonate phase in a first stage corresponds to an exothermal DTA peak at 270{degrees} C. X-ray diffraction patterns and IR spectra showed similar behavior of the powders after complete organic removal, during the conversion into perovskite phase starting at approximately 630{degrees} C and achieved about 700{degrees} C, as well as during the sintering process.