Study of the Induced Anisotropy in Field Annealed Hitperm Alloys by Mössbauer Spectroscopy and Kerr Microscopy
2016
Samples of Fe39Co39Nb6B15Cu1 alloy were nanocrystallized under zero field annealing (ZF) and transverse field annealing (TF) conditions. A reduction in coercivity for TF samples with respect to ZF sample (16 and 45 A/m, respectively) is observed. Kerr microscopy images show a well-defined parallel domain structure, transversally oriented to the ribbon axis for the TF sample unlike for the ZF sample, for which a complex pattern is observed with large and small domains at the surface of the ribbon. Although Mossbauer spectra are clearly different for the two studied samples, Mossbauer studies confirm that there is no significant difference between the hyperfine field distributions of TF and ZF samples but only the relative intensity of the 2nd and 3rd lines A 23 (related to the angle between the gamma radiation and the magnetic moments, α). However, for TF annealed samples α = 90 deg (A 23 = 4), indicating that the magnetic moments lay on the plane of the ribbon in agreement with the well-defined domain structure observed by Kerr microscopy, ZF annealed samples show A 23 = 1.8. This value is close to that of a random orientation (A 23 = 2) but smaller, indicating a slight preference for out of plane orientations. Moreover, it is clearly smaller than that of the as-cast amorphous samples A 23 = 2.8, with a preference to in-plane orientations. The application of the law of approach to saturation yields a larger effect of the inhomogeneities in ZF sample with respect to TF one.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
32
References
2
Citations
NaN
KQI