The Influence Mechanism of Temperature and Storage Period on Polarization Properties of Poly (Vinylidene Fluoride–Trifluoroethylene) Ultrathin Films

The effect of testing temperature and storage period on the polarization fatigue properties of poly (vinylidene fluoride-trifluoroethylene) (P(VDF–TrFE)) ultrathin film devices were investigated. The experimental results show that, even after stored in air for 150 days, the relative remanent polarization (Pr/Pr(0)) of P(VDF–TrFE) of ultrathin films can keep at a relatively high level of 0.80 at 25 °C and 0.70 at 60 °C. To account for this result, a hydrogen fluoride (HF) formation inhibition mechanism was proposed, which correlated the testing temperature and the storage period with the microstructure of P(VDF–TrFE) molecular chain. Moreover, a theoretical model was constructed to describe the polarization fatigue evolution of P(VDF–TrFE) samples.