COBALT CHROME AND TITANIUM CORROSION IN SCOLIOSIS CORRECTION. IS THERE A PROBLEM

Aim:The aim of this study was test the amount of corrosion occurring at the (Ti) /cobalt chrome (CoCr) interface comparing this with Ti and Ti interfaces. This was compared with retrieved metal work visualised under a scanning electron microscope (SEM).Methods:The interface of interest is the interface between rod and the screw. We investigated corrosion seen at that interface with a CoCr rod coupled to a Ti screw versus a Ti rod coupled to a Ti screw (6 screws were used) Implants were loaded according to the ASTM F2193 – 02 Standard Specifications and Test Methods for Components Used in the Surgical Fixation of the Spinal Skeletal System. Pitting potentials were monitored using cyclic potentiodynamic polarization tests (ASTM F2129 – 08 Standard Test Method for Conducting Cyclic Potentiodynamic Polarisation Measurements) to determine corrosion susceptibility. Retrieved implants were visualised under (SEM) to confirm corrosion.Results:Mean fretting current for titanium and cobalt chrome was 7.94 (μA) and f...