Surface modification of Li-rich layered Li[Li0.17Ni0.17Co0.10Mn0.56]O2 oxide with LiV3O8 as a cathode material for Li-ion batteries

Abstract A Li-rich layered oxide Li[Li 0.17 Ni 0.17 Co 0.10 Mn 0.56 ]O 2 is synthesized by a chemical deposition method. The surface modification with the LiV 3 O 8 is introduced onto Li-rich layered Li[Li 0.17 Ni 0.17 Co 0.10 Mn 0.56 ]O 2 oxide for the first time. The pristine and LiV 3 O 8 -coated Li[Li 0.17 Ni 0.17 Co 0.10 Mn 0.56 ]O 2 cathode materials are investigated by X-ray diffraction (XRD), Special surface area analysis (BET), scanning electron microscopy (SEM), transmission electron microscopy (TEM), electrochemical measurement and charge-discharge testing techniques. After coating of LiV 3 O 8 , the bulk crystallographic structure, morphology and grain size of the layered Li[Li 0.17 Ni 0.17 Co 0.10 Mn 0.56 ]O 2 are not essentially changed. Compared to the pristine sample, electrochemical performance of LiV 3 O 8 -coated samples has been obviously enhanced. Especially, the capacity retention of 3 wt% LiV 3 O 8 -coated sample reaches 94.3% after 100 charge/discharge cycles. Moreover, the rate capability is obviously increased for LiV 3 O 8 -coated samples with suitable thickness of coating. The discharge capacity of 3 wt% LiV 3 O 8 -coated sample at 2C rate is more than 157.9 mAh g −1 . Therefore, the surface modification with the LiV 3 O 8 is an effective way to improve the electrochemical performance of Li-rich layered oxides.