The influence of processing parameters on microstructural development of low-weight-percent primary, pro-eutectic, dendritic alloys during directional solidification

Alloy compositions centering about Sn- 5 to 15 wt pct Al and Pb- 4 to 20 wt pct Cu have been directionally solidified as a function of growth rate and orientation with respect to earth's gravity vector. The effect of these processing variables on macrosegregation is presented, and the consequence of a structural transition from primary columnar to equiaxed dendritic growth is examined. Effects detrimental to microstructure and attributed to density variations are shown to be minimized by a novel processing technique. In view of the ground-based results, some considerations follow regarding what might be gained by solidifying these alloys in a microgravity environment.