Characterization of age hardening mechanism of low-temperature aged low-carbon steel by transmission electron microscopy
2021
Abstract Low-temperature aging treatment at 323 K results in the dramatical increase in hardness in low-carbon ferritic steels quenched from 983 K, possibly caused by carbon clusters and/or fine e-carbides. In this study, transmission electron microscopy (TEM) analysis was carried out to characterize the change of the microstructure during the low-temperature aging treatment. Until the early stage of the peak hardness, the carbon clusters were formed homogeneously with zig-zag structures. At the latter stage of the peak hardness, it was found that the e-carbides were partially precipitated within the carbon clusters, which suggested that the carbon clusters might have acted as the precursors of e-carbides. In-situ tensile TEM observations showed that dislocation motions were free-glide type, and carbon clusters and fine-carbides interacted with dislocations via cutting-type. Dislocation interaction force was also evaluated, which suggested that the lattice misfit played as important role of the interaction mechanism.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
35
References
0
Citations
NaN
KQI