The Investigation and Growth Kinetics of TiC Coatings on AISI D3 Steel Produced by Thermo-Reactive Diffusion Technique

Abstract TiC coatings on AISI D3 cold-work tool steel were carried out by pack method thermo-reactive diffusion process (TRD) for 2 and 4 h at 950, 1 000, 1 050 and 1 100 °C, respectively. The carbide layers were evaluated based on microstructure, thickness, hardness, energy dispersive X-ray facility and X-ray diffraction analysis. Titanium carbide layer thickness on the coated specimens ranged from 6 to 23 μm, depending on treatment time and temperature. Growth kinetics of the carbide layers were analyzed measuring the depth of carbide layer as a function of temperature and time. The activation energy was estimated to be 249.42 kJ/mol. The micro-hardness value of the coating layer was obtained to be 2 470 HV in maximum.