Shaping and reinforcement of melt textured YBa2Cu3O7−δ superconductors

From porous Y2BaCuO5 (Y211) with various grain sizes, single domain ceramic composites YBa2Cu3Oy/Y2BaCuO5 have been prepared by combination of the infiltration and top seed growth (ITSG) process. In addition, perforated Y123 has been prepared from Y211 by the ITSG method in order to magnify the specific surface and then increase oxygen diffusion into the core of the material. Magnetic and electrical properties were determined and correlate well with the microstructure of the composites and were compared to the conventional doped or undoped YBa2Cu3Oy (Y123). From magnetic measurements, high critical current densities, Jc, of 86 000 A cm−2 have been measured. Transport Jc values higher than 10 600 A cm−2 are reached at 77 K and 0 T, corresponding to the nominal critical currents of 325 A injected reproducibly through sections less than 3.082 mm2. This confirms the high quality of single domains obtained with a well controlled ITSG process. On the other hand, the perforated samples were reinforced using resin impregnation and the flux mapping has been investigated.