Synthesis and properties of polyamideimides containing a bicycloöctene ring

A series of aliphatic and aromatic polyamideimides containing a bicyclooctene ring were synthesized. Low-temperature solution condensation polymerization involving various diamines and N,N′-dichloroformylmethyl-[bicyclo-(2.2.2)-oct-7-ene-2,3,5,6-tetracarb-oxylic acid 2,3,5,6-diimide] (2) were employed. Most of these polymers thus obtained were soluble in m-cresol, DMF, DMAc and DMSO etc. The inherent viscosities of the polymers ranged from 0.07 to 0.40 dl/g (in DMF at 25°C). The polymers obtained from 2 and aromatic diamines showed thermal stabilities above 380°C. The aliphatic polymers were more unstable than the aromatic polymers. Eine Reihe aliphatischer und aromatischer Polyamidimide, die einen Bicyclooctenring enthielten, wurden synthetisiert. Die Polykondensation wurde bei niedriger Temperatur in Losung durchgefuhrt, wobei eine Reihe von N,N′-Diaminen sowie N,N′-Dichlorformylmethyl-[bicyclo-(2.2.2)-oct-7-end-2,3,5,6-tetracarbonasaure-2,3,5,6-diimid] (2) eingesetzt wurden. Die meisten so erhaltenen Polymeren waren in m-Kresol, DMF, DMAc und DMSO loslich. Die Viskositatszahlen der Polymeren wurden in DMF bei 25°C bestimmt und lagen zwischen 0,07 und 0,40 dl/g. Die Polymeren aus 2 und aromatischen Diaminen zeigen thermische Stabilitaten bis uber 380°C. Die aliphatischen Polymeren waren nicht so stabil wie die aromatischen.