Effect of compression combined with steam treatment on the porosity, chemical compositon and cellulose crystalline structure of wood cell walls.

Abstract The changes of porosity, chemical composition and cellulose crystalline structure of Spruce ( Picea abies Karst.) wood cell walls due to compression combined with steam treatment (CS-treatment) were investigated by nitrogen adsorption, confocal Raman microscopy (CRM) and X-ray diffraction (XRD), respectively. A number of slit-shaped mesopores with a diameter of 3.7 nm was formed for the CS-treated wood, and more mesopores were found in the steam-treated wood. CRM results revealed cellulose structure was affected by treatment and β-aryl-ether links associated to guaiacyl units of lignin was depolymerized followed by re-condensation reactions. The crystallinity index (CrI) and crystallite thickness ( D 200 ) of cellulose for CS-treated wood were largely increased due to crystallization in the semicrystalline region. Higher degree of increase in both CrI and D 200 was observed in both the earlywood and latewood of steam-treated wood, ascribing to the greater amount of mesopores in steam-treated wood than CS-treated wood.