Improved absorbance of holmium activated magnesium-zinc-sulfophosphate glass

Constant efforts are dedicated to overcome the limitations of phosphate based glass system, where sulfophosphate glasses (SPGs) played a key role. Rare earth ions (REIs) doped magnesium zinc SPG (MZSPG) systems are technologically prospective due to their several unique attributes. Construction of integrated light amplifier and solid state laser needs the maximum gain within small component dimensions. Thus, Ho 3+ ions doped SPGs are believed to meet this demand. Ho 3+ ions having sharp optical absorption peaks in the spectral range of 200–900 nm is useful for diversified applications. Conversely, SPGs comprising of oxides of sulphur, phosphorous and at least one other component with SO 4 2- ions contents lower than PO 4 3- with low melting temperature makes them a distinctive class of technologically potential disordered system. In this view, modification of Ho 3+ ions absorbance inside SPGs network is challenging. To achieve this goal, following melt-quenching route we prepared a series of Ho 3+ -doped MZSPG system of composition (60- x )P 2 O 5 -(20)ZnSO 4 -(20)MgO–( x )Ho 2 O 3, where x = 0.0, 0.5, 1.0, 1.5 2.0, and 2.5 mol%. The influence of Ho 2 O 3 concentration on the density, refractive index, and optical absorption properties of the synthesized glass system is examined. The density and refractive index is found to increase with increasing Ho 2 O 3 concentration. The absorption spectra revealed nine prominent peaks centered at 387, 418, 450, 484, 538, 642, 1148 and 1945 nm. The glass absorbance is enhanced with increasing Ho 3+ contents. Optical band gap energy is found to range from 3.847 to 3.901 eV. The reduction of Urbach energy from 0.257 to 0.191 eV with increasing Ho 3+ contents verified the shrinkage of glass network structure and lowering of defect mediated disorder. In-depth investigations on the structural and optical properties of MZSPG system are underway to achieve the milestones set for photonic devices.