Effects of Thermal Annealing on Structural and Magnetic Properties of Lithium Ferrite Nanoparticles

Pure, crystalline, ∼10 nm lithium ferrite phase (Li0.5Fe2.5O4), was successfully synthesized at very low temperature using a modified combustion method. The crystal structure and microstructure evolution of this system upon annealing were monitored by a careful investigation of X-ray diffractograms collected on a synchrotron source. Comparative analysis of the results obtained from the full profile Rietveld method (in reciprocal space) and the pair distribution function method (in direct space) was carried out. Nanocrystalline samples exhibit similar crystal structure, on average, with a partial ordering of Li+ and Fe3+ ions between octahedral 4b and 12d sites on the spinel crystal lattice (space group P4332). After annealing at 973 K, cation distribution changes to a completely ordered, resembling that which is seen in the bulk lithium ferrite. The PDF analysis reveals abnormally high values of oxygen atomic displacement parameters in tetrahedral 8c sites (O1) indicating a significant disordering of the ...