Characterization of electron charging and transport properties of Si-QDs with phosphorus doped Ge core
2018
We formed high-density Si quantum dots (Si-QDs) with undoped and P-doped Ge cores on thermally-grown SiO2 by controlling low pressure chemical vapor depositions of Si and Ge. Doping into the Ge core was carried out during selective-growth of Ge on pre-grown Si-QDs. From hard x-ray photoelectron spectroscopy measurements, we confirmed phosphorus incorporation into the Ge core, where phosphorus donor concentration in the Ge core was roughly estimated to be ~0.09 at%. When the surfaces of Si-QDs with undoped and P-doped Ge cores were scanned with an Rh-coated tip biased at 0 V, the surface potential of Si-QDs with P-doped Ge cores were increased by ~30 mV, while that of Si-QDs with undoped Ge cores remained unchanged. These results indicate that an electron was extracted from the conduction band of the Ge core due to a phosphorus donor. In the current images measured with the Rh-coated tip, the current level of Si-QDs with P-doped Ge cores on n-Si(100) substrates was higher than that of Si-QDs with undoped Ge cores. This result indicates that phosphorus donor can contribute to an increase in the electron injection rate from the Si-substrate.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
11
References
1
Citations
NaN
KQI