Precipitation behavior and tensile property of the stress-aged Ti–10Mo–8V–1Fe–3.5Al alloy

Abstract A kind of metastable beta titanium alloy, i.e. Ti–10Mo–8V–1Fe–3.5Al, was aged under elastic compressive stress. Transmission electron microscopy (TEM) investigations revealed that, in the stress-aged samples, precipitated alpha plates were parallel to each other. However, in the conventionally aged samples, alpha plates intersected each other. In other words, variant of alpha plate was selected in the stress-aged samples. Tensile tests showed that, at equivalent tensile strength, the stress-aged samples exhibited higher ductility, compared to the conventionally aged ones.