Up-conversion emissions characteristics of non-aqueous sol-gel derived RE3Al5O12 nanocrystals.

The RE3Al5O12 (REAG:Er3Al5O12, Er:Y3Al5O12 and Er:Yb3Al5O12) up-conversion (UC) nanocrystals have been prepared by the non-aqueous sol-gel method. The green and red UC emissions are attributed to the H-2(11/2), S-4(3/2) -> I-4(15/2) and F-4(9/2) > I-4(15/2) transitions of Er3+, respectively, were obtained for all samples with a 975 nm semiconductor LD excitation. For Er3Al5O12 nanocrystals, the green and red UC emissions have similar intensities. Y and Yb ions have no evident effect on the peak positions, but strongly affected the intensities of the green and red UC emissions of the Er. A much higher intensity of the green relative to red UC emission was observed for Er:Y3Al5O12 nanocrystals, however, the red UC emission became predominant for Er:Yb3Al5O12 nanocrystals. It was suggested that the two-photon process was responsible for the green and red UC emissions mechanism for all the samples.