Strain-Driven Mn-Reorganization in Overlithiated LixMn2O4 Epitaxial Thin-Film Electrodes
2018
Lithium manganate LixMn2O4 (LMO) is a lithium ion cathode that suffers from the widely observed but poorly understood phenomenon of capacity loss due to Mn dissolution during electrochemical cycling. Here, operando X-ray reflectivity (low- and high-angle) is used to study the structure and morphology of epitaxial LMO (111) thin film cathodes undergoing lithium insertion and extraction to understand the inter-relationships between biaxial strain and Mn-dissolution. The initially strain-relieved LiMn2O4 films generate in-plane tensile and compressive strains for delithiated (x 1) charge states, respectively. The results reveal reversible Li insertion into LMO with no measurable Mn-loss for 0 1) reveals Mn loss from LMO along with dramatic changes in the intensity of the (111) Bragg peak that cannot be explained by Li stoichiometry. These results reveal a partially reversible site reorganization of Mn ions within the LMO fil...
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
54
References
8
Citations
NaN
KQI