The effect of graphene for the hydrogen evolution reaction in alkaline medium
2016
Abstract In this work, Ni-graphene (Ni-G) composites were prepared on the surface of 304 stainless steel (304 SS) by using a simple, economical and effective electrodeposition technique in a Ni based bath with deposition time from 1 min to 30 min. The effect of graphene for hydrogen evolution reaction (HER) was researched. Graphene content in the Ni-G composite coatings with deposition time of 1 min, 5 min and 30 min was 0.42 at%, 1.47 at% and 2.82 at%, respectively. With the increase of graphene content in the Ni-G composite coatings, the onset overpotential was decreased and exchange current density was enhanced during the HER. The minimum onset overpotential and maximum exchange current density of Ni-G/304 SS for the HER was 75 mV and 1.43 mA cm 2 in 0.1 mol L −1 KOH solution at 298.15 K. The best Ni-G/304 SS exhibited a maximum current density of 9.50 mA cm −2 at 1.3 V, which was approximately 7.4 times higher than that of Ni/304 SS, indicating the best activity for hydrogen production. Comparing with the HER of Ni/304 SS and 304 SS, the maximum current density on the Ni-G/304 SS was 18.6 times higher than that on the Ni/304 SS and 12.3 times higher than that on the 304 SS, after starting HER for 60 min. High catalytic activity was attributed to the structural advantages of Ni-G/304 SS, including high specific surface areas and excellent electrical conductivity.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
25
References
43
Citations
NaN
KQI