Spray Forming of Homogeneous 20MnCr5 Steel of Low Distortion Potential

Spray forming is an advanced technology for the manufacture of homogeneous material from the melt. In this study, 20MnCr5 steel, a typical case hardening steel for gear and shaft production, has been spray formed and hot worked to semi-finished bars. Shaft-like specimens have been made from the spray-formed material for distortion investigation. Material characteristics of the spray-formed 20MnCr5 steel have been studied. In cooperation with other projects of the Collaborative Research Center SFB570 ‘’Distortion Engineering’’, evaluation of distortion behavior of the shaft specimens after machining and heat treatment has been made in comparison with continuous cast material. Spray-formed 20MnCr5 steel shows lower distortion potential due to improved material homogeneity. Spruhkompaktieren von homogenem 20MnCr5 Stahl mit geringem Verzugspotenzial Spruhkompaktieren ist eine neue Technologie zur Herstellung von homogenen Werkstoffen aus der Schmelze. In dieser Arbeit wurde der 20MnCr5, ein typischer Einsatzstahl zur Herstellung von Zahnradern und Wellen, spruhkompaktiert und warmumgeformt, um Rundstabe als Halbzeug zu erhalten. Aus diesem Material wurden wellenformige Proben gefertigt, ihre Mas- und Formanderung untersucht und Werkstoffeigenschaften des spruhkompaktierten 20MnCr5 analysiert. In Zusammenarbeit mit weiteren Projekten des Sonderforschungsbereichs SFB 570 „Distortion Engineering” erfolgte die Auswertung des Verzugsverhaltens der Wellen nach Fertigung und Warmebehandlung im Vergleich mit Halbzeug, das aus Strangguss erzeugt wurde. Der spruhkompaktierte Stahl 20MnCr5 zeigt aufgrund seiner verbesserten Werkstoffhomogenitat das niedrigere Verzugspotenzial.